ANALISIS VARIASI ALIRAN GAS PELINDUNG DAN BENTUK KAMPUH PADA PROSES LAS GMAW TERHADAP KEKERASAN DAN STRUKTUR MIKRO BAJA ASTM A36
Abstract
This study aims to determine the effect of variations in the protective gas flow and seam formation on the hardness and microstructure of ASTM A36 steel. The variation of the protective gas flow used is 5 liters/minute, 10 liters/minute, and 15 liters/minute, while the form of seam used is seam I, ½ V, and V with ER 70S-6 electrodes with a diameter of 1.2 mm. The results showed that the greater protective gas flow would increase the value of violence. The highest increase in weld metal and HAZ hardness was in seam V with 15 liters/minute gas flow as much as 38.06% weld metal, 11.15% HAZ, while the lowest hardness value of weld metal was in gas flow 5 liters/minute at seam ½ V is 41.9 HRB and the lowest HAZ hardness value is in the gas flow of 5 liters/minute in Kampung I which is 40.8 HRB. The highest increase in hardness of base metal was in ½ V with 39.46% with 15 liters/minute gas flow, while the lowest base metal hardness was in Kampung I, 43.4 HRB with 5 liters/minute gas flow. The structural test results show the higher the protective gas flow will increase the formation of more pearlite. The highest percentage of pearlite formation is in the weld metal of seam V, which is 53.16% and the percentage of pearlite at least in the HAZ area of ​​seam I is 38.17%.
Downloads
References
Z. Fakri, Bukhari and N. Juhan, "Analisa Pengaruh Kuat Arus Pengelasan GMAW Terhadap Ketangguhan Sambungan Baja AISI 1050," Journal of Welding Technology, Vol. 1, No. 1, pp. 5-10, 2019.
H. Wiryosumarto and T. Okumura, Teknologi Pengelasan Logam, Jakarta: PT. Pradnya Paramita, 2000.
S. Surapranata, Pengelasan Pelat Menggunakan Proses GMAW (Gas Metal Arc Welding), Jakarta: Modul Pelatihan Guru, Direktorat Jenderal Guru dan Tenaga Kependidikan, 2015.
H. R. Setiawan, Pengaruh Variasi Kampuh Terhadap Kekerasan Baja ST60 Menggunakan Las Listrik Posisi 3G, Banjarbaru: Tugas Akhir, Teknik Mesin, Universitas Lambung Mangkurat, 2014.
A. N. Khiyaarul, N. Syahroni and Y. S. Hadiwidodo, "Analisis Pengaruh Variasi Flow Rate Gas Pelindung pada Pengelasan FCAW-G terhadap Struktur Mikro dan Kekuatan Mekanik Sambungan Material Grade A," Jurnal TEKNIK ITS, Vol. 7, No. 2, pp. 186-191, 2018.
A. W. Prasetya , Rusiyanto and Pramono, "Pengaruh Debit Gas Pelindung dan Tegangan Listrik Terhadap Tingkat Kekerasan dan Struktur Mikro Sabungan Las GMAW Pada Baja Karbon Sedang EMS-45," Jurnal Kompetensi Teknik, Vol. 8, No. 2, pp. 27-51, 2017.
R. Siswanto , "Pengaruh Bentuk Kampuh Terhadap Panjang, Kedalaman Penetrasi dan Lebar Hasil Pengelasan Menggunakan Las Busur Listrik (SMAW)," Jurnal Fisika FLUX, Vol. 9, No. 1, pp. 151-158, 2012.
J. Arifin, H. Purwanto and I. Syafa'at, "Pengaruh Jenis Elektroda Terhadap Sifat Mekanik Hasil Pengelasan SMAW Baja ASTM A36," Momentum, Vol. 13, No. 1, pp. 27-31, 2017.
Copyright (c) 2020 sjme KINEMATIKA
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.