UJI KEKERASAN PADA Al-Cu HASIL PENGECORAN METODE DIE CASTING DENGAN VARIASI TEMPERATUR TUANG DAN TEKANAN

  • Akhmad Taufik Universitas Lambung Mangkurat
  • Ma'ruf Ma'ruf Universitas Lambung Mangkurat
Keywords: die casting, Al-Cu, pour temperature, pressure, hardness value

Abstract

In the automotive industry, the component parts and engine elements mostly use aluminum alloys with the casting process, one of which is aluminum with copper (Al-Cu) aluminum alloys. Metal casting die casting method is part of pressurized casting, where the metal is pressed into the mold. Many aluminum casting industries, especially small and medium industries, in the manufacture of products or components use recycled materials by the casting foundry method, so that they will affect the decrease in material properties. The die casting method is expected to be able to improve its physical and mechanical properties. The casting process using the die casting method is carried out at pour temperature (650â°C, 670â°C, and 690â°C) with variations in pressure 0 (no pressure), 2.5 MPa, 5 MPa and 7.5 MPa. The results of the hardness test showed that the pouring temperature was 650â°C and 7.5 MPa pressure was the highest hardness with a value of 72 HB and the lowest hardness value was at a temperature of 690â°C without pressure with a hardness value of 58 HB. From this study it can be concluded that the pouring temperature and pressure are very influential on the value of hardness in the casting process by die casting method.

Downloads

Download data is not yet available.

References

R. Siswanto, A. Ghofur and K. A. K. Kepakisa, "Analisis Porositas Dan Kerasan Paduan Al-12, 6% Si Dengan Variasi Waktu Tunggu Dalam Cetakan Dan Media Pendingin Hasil Pengecoran Evaporative," Jukung Jurnal Teknik Lingkungan, vol. 4(1), pp. 72-81, 2018.

L. P. Hartono, H. Purwanto and S. M. B. Respati, "Pengaruh Tekanan Terhadap Struktur Mikro dan Kekerasan pada Proses Semi Solid Die Casting pada Paduan Aluminium Daur Ulang," Momentum, vol. 8, pp. 35-42, 2012.

M. R. F. Putra, W. Suprapto and A. A. Sonief, "Pengaruh Kecepatan Pengadukan Proses Rheocasting Terhadap Struktur Mikro dan Fluiditas Paduan Al-Cu," Rekayasa Mesin, vol. 10, pp. 257-263, 2019.

T. Surdia and K. Chijiwa, Teknik Pengecoran Logam, Jakarta: PT Pradnya Paramita, 2000.

H. Utama, "Pengaruh Penambahan Cu (1%, 3% dan 5%) pada Aluminium dengan Solution Heat Treatment dan Natural Aging Terhadap Sifat Fisis dan Mekanis," 2009.

S. Drihandono and E. Budiyanto, "Pengaruh Temperatur Tuang, Temperatur Cetakan, dan Tekanan Pada Pengecoran Bertekanan (High Pressure Die Casting/HPDC) Terhadap Kekerasan dan Struktur Mikro Aluminium Paduan Silikon (Al-Si 7,79%)," Turbo, vol. 5, pp. 30-38, 2016.

S. B. Respati, H. Purwanto and M. S. Mauluddin, "Pengaruh Tekanan dan Temperatur Cetakan Terhadap Struktur Mikro dan Kekerasan Hasil Pengecoran pada Material Aluminium Daur Ulang," Prosiding Seminar Nasional & Internasional, vol. 3, pp. 284-289, Januari 2010.

Published
2021-06-30
How to Cite
[1]
Akhmad Taufik and M. Ma’ruf, “UJI KEKERASAN PADA Al-Cu HASIL PENGECORAN METODE DIE CASTING DENGAN VARIASI TEMPERATUR TUANG DAN TEKANAN”, SJMEkinematika, vol. 6, no. 1, pp. 33-42, Jun. 2021.