PENGARUH VARIASI TEMPERATUR PEMANASAN DAN MEDIA PENDINGIN TERHADAP KEKERASAN DAN STRUKTUR MIKRO BAJA ST 41 METODE HARDENING
Abstract
ST 41 steel is one of the types of low carbon steel group whose mechanical properties can be improved by means of the heat treatment process. Hardening is a heat treatment process that aims to increase the hardness and strength of steel by heating, holding and cooling in certain time intervals and cooling media. The purpose of this study was to determine the effect of heating temperature and cooling media on the hardness and microstructure of ST 41 steel. The hardening process was carried out at austenite temperatures(850oC, 900oC and 950oC) with a holding time of 15 minutes then cooled quickly using a cooling medium of distilled water, SAE oil 20W-50, and coconut water. The test results show the optimum hardness value is 326.2 HV at 850oC heating temperature with water cooling media and a minimum hardness of 153.1 HV at 950oC heating temperature with SAE 20W-50 oil cooling media, while the
results of microstructure testing after the hardening process show that the structure formed are martensite and bainite. From this study it can be concluded that the hardening process can increase the value of hardness in ST 41 steel.
Downloads
References
H. Purwanto, Diktat Material Teknik. Semarang: Teknik Mesin UNWAHAS, 2012.
A. Mustofa, S. Jokosisworo, and A. Wibawa Budi S., “Jurnal teknik perkapalan,†Tek. Perkapalan, vol. 6, no. 2, pp. 199–206, 2018.
W. D. Callister, Materials science and engineering: An introduction (8th edition), vol. 12, no. 1. Hoboken: John Wiley & Sons, Inc, 2009.
F. . Campbell, Elements of Metallurgy and Engineering Alloys. SM International, 2008.
R. Adawiyah, Murdjani, and A. Hendrawan, “Pengaruh Perbedaan Media Pendingin Terhadap Strukturmikro Dan Kekerasan Pegas Daun Dalam Proses Hardening,†Poros Tek., vol. 6, no. 2, pp. 88–95, 2014.
M. Bahtiar and Supramono, “Pengaruh media pendingin minyak pelumas sae 40 pada proses quenching dan tempering terhadap ketangguhan baja karbon rendah,†2014.
A. Pramono, “Karakteristik Mekanik Proses Hardening Baja Aisi 1045 Media Quenching Untuk Aplikasi Sprochet Rantai,†J. Ilm. Tek. Mesin Cakra M, vol. 5, no. 1, pp. 32–38, 2011.
I. K. Suarsana, I. N. Santhiarsa, and D. P. Negara, “Pengaruh Perlakuan Temperatur dan Media Pendinginan Terhadap Sifat Ketangguhan Baja AISI 3215,†J. METTEK, vol. 4, no. 1, p. 23, 2018, doi: 10.24843/mettek.2018.v04.i01.p04.
Copyright (c) 2020 sjme KINEMATIKA
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.