ANALISIS VARIASI KECEPATAN WIRE FEEDER PADA PROSES LAS GMAW TERHADAP KEKERASAN DAN STRUKTUR MIKRO BAJA ASTM A36
Abstract
This study aims to determine the effect of variations in wire feeder speed on the GMAW welding process on the hardness and microstructure of ASTM A36 steel. Wire feeder variations used are 3.5 meters / minute, 3.55 meters / minute and 3.6 meters / minute, ER 70S-6 electrodes with a diameter of 1.2 mm. The results showed that the highest hardness value in weld metal was found in specimen 1 wire feeder speed of 3.5 meters / minute with hardness value of 59.5 HRB. The highest hardness value in the HAZ area is in specimen 3 with a wire feeder speed of 3.6 meters / minute with a hardness value of 57.5 HRB. While the highest base metal hardness value is in the specimen 3 wire feeder speed of 3.55 meters / minute with a hardness value of 64.4 HRB. Microstructure observation results show that the higher the hardness value will increase the pearlite phase more and vice versa the lower the hardness value the ferrite phase is more than the pearlite phase.
Downloads
References
A. S. Bagaskoro, D. R. B. P and A. Widyianto, "Analisis pengaruh arus dan kecepatan pengelasan terhadap lebar manik las dan distorsi pada pengelasan gas metal arc welding (GMAW) dengan sambungan tumpul SS 304," Jurnal Teknik Mesin Indonesia, vol. 14, no. 2, pp. 52-57, 2019.
F. B. Susetyo, "Efek Variasi Kecepatan Wire Feeder GMAW Terhadap Tensile Strength ASTM A36," Jurnal Konversi Energi dan Manufaktur UNJ, 2017.
Budiarsa, I N., "Pengaruh besar arus pengelasan dan kecepatan volume air gas pada proses las GMAW terhadap ketangguhan baja ASTM A36"," Jurusan Teknik Mesin CAKRAM, vol. 2, pp. hlm 112-116, 2008.
Wijoyo and B. K. Aji, "Kajian Kekerasan Dan Struktur Mikro Sambungan Las GMAW Baja Karbon Tinggi Dengan Variasi Masukan Arus Listrik," Jurnal SIMETRIS, vol. 6, no. 2, 2015.
A. W. Prasetya, Rusiyanto and Pramono, "Pengaruh debit aliran gas pelindung dan tegangan listrik terhadap tingkat kekerasan dan struktur mikro sambungan las GMAW pada baja karbon sedang EMS-45," Jurnal Kompetensi Teknik, vol. 8, no. 2, 2017.